Photoresist composition and associated method of forming an electronic device

ABSTRACT

A photoresist composition includes a first polymer in which at least half of the repeat units are photoacid-generating repeat units, and a second polymer that exhibits a change in solubility in an alkali developer under the action of acid. In the first polymer, each of the photoacid-generating repeat units comprises photoacid-generating functionality and base-solubility-enhancing functionality.

FIELD

The present invention relates to a photoresist composition comprising a photoacid-generating polymer.

INTRODUCTION

As feature sizes of integrated circuits continue to shrink, next generation lithographic processes struggle to fit the stringent requirements to extend Moore's Law. It has long been recognized that increased photoacid generator (PAG) non-uniformity and acid diffusion have limited photoresist resolution, worsened line width roughness (LWR) (see, e.g., Nakamura et. al., Proc. SPIE 2013, 8682, 86821H-1), limited exposure latitude, and generally degraded photolithographic performance for chemically amplified resists. In the past, polymer-bound-PAG (PBP) systems have been implemented to increase PAG uniformity and control acid diffusion (see, e.g., Oh et. al., Proc. SPIE 2008, 7140 714031, pages 1-9; and U.S. Pat. No. 5,945,250 B2 to Aoai et al.). More recently, increased concentration of PAG in the matrix has been shown to further enhance lithographic performance, particularly when combined with a PBP system (U.S. Patent Application Publication No. US 2014/0080062 A1 of Thackeray et al.). Despite these advances, there remains a need for photoresist compositions providing one or more of decreased critical dimension uniformity, increased contact hole exposure latitude, increased line-space exposure latitude, and decreased line width roughness.

SUMMARY

One embodiment is a photoresist composition comprising: a first polymer comprising, based on 100 mole percent of total repeat units, 50 to 100 mole percent of photoacid-generating repeat units; wherein each of the photoacid-generating repeat units comprises an anion, a photoacid-generating cation, and base-solubility-enhancing functionality; wherein either the anion or the photoacid-generating cation is polymer-bound; wherein the base-solubility-enhancing functionality is selected from the group consisting of tertiary carboxylic acid esters, secondary carboxylic acid esters wherein the secondary carbon is substituted with at least one unsubstituted or substituted C₆₋₄₀ aryl, acetals, ketals, lactones, sultones, alpha-fluorinated esters, beta-fluorinated esters, alpha,beta-fluorinated esters, polyalkyleneglycols, alpha-fluorinated alcohols, and combinations thereof; and wherein the photoacid-generating cation has the structure (I)

wherein q is independently in each photoacid-generating repeat unit 0, 1, 2, 3, 4, or 5; r is independently at each occurrence in each photoacid-generating repeat unit 0, 1, 2, 3, or 4; R¹ is independently at each occurrence in each photoacid-generating repeat unit halogen, unsubstituted or substituted C₁₋₄₀ hydrocarbyl, or unsubstituted or substituted C₁₋₄₀ hydrocarbylene; m is independently in each photoacid-generating repeat unit 0 or 1; X is independently in each photoacid-generating repeat unit a single bond, —O—, —S—, —C(═O)—, —C(R²)₂—, —C(R²)(OH)—, —C(═O)O—, —C(═O)N(R²)—, —C(═O)C(═O)—, —S(═O)—, or —S(═O)₂—, wherein R² is independently at each occurrence hydrogen or C₁₋₁₂ hydrocarbyl; and Z⁻ is free or monovalent monoanion; and a second polymer that exhibits a change in solubility in an alkali developer under the action of acid.

Another embodiment is a method of forming an electronic device, comprising: (a) applying a layer of the photoresist composition on a substrate; (b) pattern-wise exposing the photoresist composition layer to activating radiation; and (c) developing the exposed photoresist composition layer to provide a resist relief image.

These and other embodiments are described in detail below.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a synthetic scheme for the preparation of 5-(3,5-dimethyl-4-(2-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-2-oxoethoxy)phenyl)-5H-dibenzo[b,d]thiophen-5-ium ((1S,4S)-7,7-dimethyl-2-oxobicyclo[2.2.1]heptan-1-yl)methanesulfonate.

FIG. 2 is a synthetic scheme for the preparation of 2-(2-methoxyethoxy)ethyl 4-tosylate.

FIG. 3 is a synthetic scheme for the preparation of 2-(2-(2-methoxyethoxy)ethoxy)-1,3-dimethylbenzene.

FIG. 4 is a synthetic scheme for the preparation of 5-(4-(2-(2-methoxyethoxy)ethoxy)-3,5-dimethylphenyl)-dibenzothiophen-5-ium iodide.

FIG. 5 is a synthetic scheme for the preparation of 5-(4-(2-(2-methoxyethoxy)ethoxy)-3,5-dimethylphenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate.

FIG. 6 is a synthetic scheme for the preparation of 5-(4-methoxy-3-(4-(2-methyladamantan-2-yl)oxy)-1-(2-((2-methyladamantan-2-yl)oxy)-2-oxoethoxy)-1,4-dioxobutan-2-yl)phenyl)-dibenzothiophenium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate.

FIG. 7 is a synthetic scheme for the preparation of 5-(4-methoxy-3-(4-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-1-(2-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-2-oxoethoxy)-1,4-dioxobutan-2-yl)phenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(2-(methacryloyloxy)acetoxy)ethanesulfonate.

FIG. 8 is a synthetic scheme for the preparation of 5-(4-methoxy-3-(2-(2-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-2-oxoethoxy)-2-oxo-1-(2-oxotetrahydrofuran-3-yl)ethyl)phenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate.

FIG. 9 is a synthetic scheme for the preparation of a homopolymer of 5-(4-methoxy-3-(4-((2-methyladamantan-2-yl)oxy)-1-(2-((2-methyladamantan-2-yl)oxy)-2-oxoethoxy)-1,4-dioxobutan-2-yl)phenyl)-dibenzothiophenium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate.

FIG. 10 is a synthetic scheme for the preparation of a homopolymer of 5-(4-methoxy-3-(4-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-1-(2-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-2-oxoethoxy)-1,4-dioxobutan-2-yl)phenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(2-(methacryloyloxy)acetoxy)ethanesulfonate.

FIG. 11 is a synthetic scheme for the preparation of a homopolymer of 5-(4-methoxy-3-(2-(2-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-2-oxoethoxy)-2-oxo-1-(2-oxotetrahydrofuran-3-yl)ethyl)phenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate.

FIG. 12 is a synthetic scheme for the preparation of a copolymer of 5-(4-(2-(2-methoxyethoxy)ethoxy)-3,5-dimethylphenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate and 5-(4-methoxy-3-(4-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-1-(2-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-2-oxoethoxy)-1,4-dioxobutan-2-yl)phenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(2-(methacryloyloxy)acetoxy)ethanesulfonate.

FIG. 13 is a synthetic scheme for the preparation of a Copolymer 5-(4-(2-(2-methoxyethoxy)ethoxy)-3,5-dimethylphenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate and 5-(4-methoxy-3-(2-(2-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-2-oxoethoxy)-2-oxo-1-(2-oxotetrahydrofuran-3-yl)ethyl)phenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate.

DETAILED DESCRIPTION

The present inventors have determined that the photolithographic performance of a photoresist composition can be improved by the incorporation of a first polymer in which at least 50 mole percent of the repeat units are photoacid-generating repeat units, and a second polymer that exhibits a change in solubility in an alkali developer under the action of acid. In the first polymer, each of the photoacid-generating repeat units comprises photoacid-generating functionality and base-solubility-enhancing functionality. The improvement in photolithographic performance can be manifested as one or more of decreased critical dimension uniformity, decreased dose to clear energy, and increased contrast slope.

Thus, one embodiment is a photoresist composition comprising: a first polymer comprising, based on 100 mole percent of total repeat units, 50 to 100 mole percent of photoacid-generating repeat units; wherein each of the photoacid-generating repeat units comprises an anion, a photoacid-generating cation, and base-solubility-enhancing functionality; wherein either the anion or the photoacid-generating cation is polymer-bound; wherein the base-solubility-enhancing functionality is selected from the group consisting of tertiary carboxylic acid esters, secondary carboxylic acid esters wherein the secondary carbon is substituted with at least one unsubstituted or substituted C₆₋₄₀ aryl, acetals, ketals, lactones, sultones, alpha-fluorinated esters, beta-fluorinated esters, alpha,beta-fluorinated esters, polyalkyleneglycols, alpha-fluorinated alcohols, and combinations thereof; and wherein the photoacid-generating cation has the structure (I)

wherein q is independently in each photoacid-generating repeat unit 0, 1, 2, 3, 4, or 5; r is independently at each occurrence in each photoacid-generating repeat unit 0, 1, 2, 3, or 4; R¹ is independently at each occurrence in each photoacid-generating repeat unit halogen, unsubstituted or substituted C₁₋₄₀ hydrocarbyl, or unsubstituted or substituted C₁₋₄₀ hydrocarbylene; m is independently in each photoacid-generating repeat unit 0 or 1; X is independently in each photoacid-generating repeat unit a single bond, —O—, —S—, —C(═O)—, —C(R²)₂—, —C(R²)(OH)—, —C(═O)O—, —C(═O)N(R²)—, —C(═O)C(═O)—, —S(═O)—, or —S(═O)₂—, wherein R² is independently at each occurrence hydrogen or C₁₋₁₂ hydrocarbyl; and Z⁻ is free or monovalent monoanion; and a second polymer that exhibits a change in solubility in an alkali developer under the action of acid.

Within the range of 50 to 100 mole percent, the content of photoacid-generating repeat units in the first polymer can be 60 to 100 mole percent, specifically 70 to 100 mole percent, more specifically 80 to 100 mole percent, even more specifically 90 to 100 mole percent, still more specifically 95 to 100 mole percent. As used herein, the term “repeat unit” refers to divalent unit that is the residue of a polymerizable monomer. Conversely, “repeat unit” does not include monovalent groups, such as a terminal group derived from a polymerization initiator.

Each of the photoacid-generating repeat units of the first polymer comprises an anion, a photoacid-generating cation, and base-solubility-enhancing functionality. The combination of the anion and the photoacid-generating cation has the structure (I)

wherein q is independently in each photoacid-generating repeat unit 0, 1, 2, 3, 4, or 5; r is independently at each occurrence in each photoacid-generating repeat unit 0, 1, 2, 3, or 4; R¹ is independently at each occurrence in each photoacid-generating repeat unit halogen, unsubstituted or substituted C₁₋₄₀ hydrocarbyl, or unsubstituted or substituted C₁₋₄₀ hydrocarbylene; m is independently in each photoacid-generating repeat unit 0 or 1; X is independently in each photoacid-generating repeat unit a single bond, —O—, —S—, —C(═O)—, —C(R²)₂—, —C(R²)(OH)—, —C(═O)O—, —C(═O)N(R²)—, —C(═O)C(═O)—, —S(═O)—, or —S(═O)₂—, wherein R² is independently at each occurrence hydrogen or C₁₋₁₂ hydrocarbyl; and Z⁻ is a free or monovalent monoanion. As used herein, the term “hydrocarbyl”, whether used by itself, or as a prefix, suffix, or fragment of another term, refers to a residue that contains only carbon and hydrogen unless it is specifically identified as “substituted hydrocarbyl”. The hydrocarbyl residue can be aliphatic or aromatic, straight-chain, cyclic, bicyclic, branched, saturated, or unsaturated. It can also contain combinations of aliphatic, aromatic, straight chain, cyclic, bicyclic, branched, saturated, and unsaturated hydrocarbon moieties. When the hydrocarbyl residue is described as substituted, it can contain heteroatoms in addition to carbon and hydrogen.

When the photoacid-generating cation is polymer-bound, then the photoacid-generating cation is monovalent and Z⁻ is a free monoanion. Conversely, when Z⁻ is polymer bound, then the photoacid-generating cation is a free cation, and Z⁻ is a monovalent monoanion.

The anion Z⁻ can comprise sulfonate (—SO₃), sulfonamidate (anion of sulfonamide; —S(O)₂N⁻R³, wherein R³ is H or unsubstituted or substituted C₁₋₁₂ hydrocarbyl), or sulfonimidate (anion of sulfonimide; —S(O)₂N⁻S(O)₂R³, wherein R³ is H or unsubstituted or substituted C₁₋₁₂ hydrocarbyl).

In addition to photoacid-generating functionality, each photoacid-generating repeat unit of the first polymer comprises base-solubility-enhancing functionality. Base-solubility-enhancing functionality includes functional groups that are base-soluble (e.g., polyalkyleneglycols, alpha-fluorinated alcohols); functional groups that are base-soluble after acid-catalyzed deprotection (e.g., tertiary esters, acetals, ketals, secondary carboxylic acid esters wherein the secondary carbon is substituted with at least one unsubstituted or substituted C₆₋₄₀ aryl); and functional groups that are base-soluble after base-catalyzed deprotection (e.g., fluorinated esters, lactones, sultones). Examples of base-solubility-enhancing functionality include tertiary carboxylic acid esters, secondary carboxylic acid esters wherein the secondary carbon is substituted with at least one unsubstituted or substituted C₆₋₄₀ aryl, acetals, ketals, lactones, sultones, alpha-fluorinated esters, beta-fluorinated esters, alpha,beta-fluorinated esters, polyalkyleneglycols, alpha-fluorinated alcohols, and combinations thereof. In some embodiments, the base-solubility-enhancing functionality is a tertiary carboxylic acid ester, an acetal, a ketal, a lactone, or a combination thereof. In some embodiments, the base-solubility-enhancing functionality is a tertiary carboxylic acid ester, a lactone, or a combination thereof. The base-solubility-enhancing functionality can reside in the anion or the photoacid-generating cation. In some embodiments, base-solubility-enhancing functionality resides in the photoacid-generating cation.

In some embodiments of the first polymer, the photoacid-generating repeat units are derived from a single monomer. Alternatively, the photoacid-generating repeat units can be derived from at least two different monomers.

The polymer comprises 50 to 100 mole percent of photoacid-generating repeat units, based on 100 mole percent of total repeat units. When the polymer comprises less than 100 mole percent of photoacid generating repeat units, the other repeat units can comprise photoacid-generating functionality or not, and they can comprise base-solubility-enhancing functionality or not. Examples of monomers from which such other repeat units can be derived are

wherein each occurrence of R^(a) is independently H, F, —CN, C₁₋₁₀ alkyl, or C₁₋₁₀ fluoroalkyl.

In some embodiments, the first polymer has a weight average molecular weight of 2,500 to 10,000 daltons, specifically 3,000 to 7,000 daltons.

In some embodiments, the photoacid-generating functionality of the first polymer comprises a polymer-bound anion and a non-polymer-bound cation. For example, in some embodiments, each of the photoacid-generating repeat units independently has the structure

wherein R³ is independently in each of the repeat units H, F, —CN, C₁₋₁₀ alkyl, or C₁₋₁₀ fluoroalkyl; n is independently in each of the repeat units 0 or 1; L¹ and L³ are each independently in each of the repeat units an unsubstituted or substituted C₁₋₂₀ hydrocarbylene, wherein the substituted C₁₋₂₀ hydrocarbylene can, optionally, comprise one or more in-chain divalent heteroatom-containing groups that is —O—, —S—, —NR⁴, —PR⁴—, —C(O)—, —OC(O)—, —C(O)O—, —OC(O)O—, —N(R⁴)C(O)—, —C(O)N(R⁴)—, —OC(O)N(R⁴)—, —N(R⁴)C(O)O—, —S(O)—, —S(O)₂—, —N(R⁴)S(O)₂—, —S(O)₂N(R⁴)—, —OS(O)₂—, or —S(O)₂O—, wherein R⁴ is H or C₁₋₁₂ hydrocarbyl; L² is independently in each of the repeat units —O—, —C(O)—, or —N(R⁵)—, wherein R⁵ is H or C₁₋₁₂ hydrocarbyl; and q, r, R¹, m, and X are defined for structure (I).

In other embodiments, the photoacid-generating functionality of the first polymer comprises a polymer-bound cation and a non-polymer-bound anion. For example, in some embodiments, in each of the photoacid-generating repeat units one occurrence of R¹ is present in structure (II) or (II) (i.e., one occurrence of R¹ is associated with a non-zero occurrence of q or r), covalently links the photoacid-generating cation to the polymer, and has the structure

wherein R³ is independently in each of the repeat units H, F, —CN, C₁₋₁₀ alkyl, or C₁₋₁₀ fluoroalkyl; L⁴ is independently in each of the repeat units 1,2-phenylene, 1,3-phenylene, 1,4-phenylene, —C(O)O—, —C(O)C(O)—, or —C(O)N(R⁵)—, wherein R⁵ is H or C₁₋₁₂ hydrocarbyl; p is independently in each of the repeat units 0 or 1; and L⁵ is independently in each of the repeat units an unsubstituted or substituted C₁₋₂₀ hydrocarbylene, wherein the substituted C₁₋₂₀ hydrocarbylene can, optionally, comprise one or more in-chain divalent heteroatom-containing groups that is —O—, —S—, —NR⁴, —PR⁴—, —C(O)—, —OC(O)—, —C(O)O—, —OC(O)O—, —N(R⁴)C(O)—, —C(O)N(R⁴)—, —OC(O)N(R⁴)—, —N(R⁴)C(O)O—, —S(O)—, —S(O)₂—, —N(R⁴)S(O)₂—, —S(O)₂N(R⁴)—, —OS(O)₂—, or —S(O)₂O—, wherein R⁴ is H or C₁₋₁₂ hydrocarbyl.

In specific embodiments, the first polymer comprises a homopolymer of 5-(4-methoxy-3-(4-((2-methyladamantan-2-yl)oxy)-1-(2-((2-methyladamantan-2-yl)oxy)-2-oxoethoxy)-1,4-dioxobutan-2-yl)phenyl)-dibenzothiophenium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate, a homopolymer of 5-(4-methoxy-3-(4-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-1-(2-(((1R,3 S,5r,7r)-2-methyladamantan-2-yl)oxy)-2-oxoethoxy)-1,4-dioxobutan-2-yl)phenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(2-(methacryloyloxy)acetoxy)ethanesulfonate, a homopolymer of 5-(4-methoxy-3-(2-(2-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-2-oxoethoxy)-2-oxo-1-(2-oxotetrahydrofuran-3-yl)ethyl)phenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate, a copolymer of 5-(4-(2-(2-methoxyethoxy)ethoxy)-3,5-dimethylphenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate and 5-(4-methoxy-3-(4-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-1-(2-(((1R,3 S,5r,7r)-2-methyladamantan-2-yl)oxy)-2-oxoethoxy)-1,4-dioxobutan-2-yl)phenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(2-(methacryloyloxy)acetoxy)ethanesulfonate, a copolymer 5-(4-(2-(2-methoxyethoxy)ethoxy)-3,5-dimethylphenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate and 5-(4-methoxy-3-(2-(2-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-2-oxoethoxy)-2-oxo-1-(2-oxotetrahydrofuran-3-yl)ethyl)phenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate, or a combination thereof.

In addition to the first polymer, the photoresist composition comprises a second polymer. The second polymer exhibits a change in solubility in an alkali developer under the action of acid. The alkali developer can be, for example, 0.26 Normal aqueous TMAH. The acid can be generated by exposure of the photoacid-generating functionality in the photoresist composition to activating radiation. The photoacid-generating functionality can be in the photoacid-generating repeat units, in the second polymer, or in a non-polymer-bound photoacid generator. The change in solubility of the second polymer can be due to the reaction of photo-generated acid with acid-labile functionality in the second polymer. For example, the second polymer can comprise a tertiary carboxylic acid ester, a secondary carboxylic acid ester wherein the secondary carbon is substituted with at least one unsubstituted or substituted C₆₋₄₀ aryl, an acetal, a ketal, or a combination thereof. Further change in solubility of the second polymer can be due to ionization or reaction of second polymer functional groups with the base in the alkali developer. For example, a tertiary carboxylic acid ester in the second polymer can react with acid to form a carboxylic acid and a tertiary alcohol, and the carboxylic acid can react with base to form a carboxylate anion.

In specific embodiments, the second polymer comprises 1 to 70 mole percent of acid-labile repeat units, 0 to 60 mole percent of base-labile repeat units, 0 to 60 mole percent of base-soluble repeat units, and 0 to 50 mole percent of photoacid-generating repeat units, wherein the sum of acid-labile repeat units, base-labile repeat units, base-soluble repeat units, and photoacid-generating repeat units in the second polymer is 100 mole percent.

In more specific embodiments, the second polymer comprises 10 to 65 mole percent of acid-labile repeat units, 0 to 50 weight percent of base-labile repeat units, 0 to 40 mole percent of base-soluble repeat units, and 1 to 15 mole percent, specifically 2 to 10 mole percent, of photoacid-generating repeat units.

In addition to the first polymer and the second polymer, photoresist composition optionally further includes a photo-destroyable quencher, an amine or amide additive to adjust photospeed and/or acid diffusion, a solvent, a surfactant, or a combination thereof.

The photoresist composition can include an amine or amide compound. These compounds are sometimes referred to as “quenchers” but are chemically distinct from the photo-destroyable quencher. The amine or amide compounds include C₁₋₃₀ organic amines, imines, or amides, or can be a C₁₋₃₀ quaternary ammonium salt of a strong base (e.g., a hydroxide or alkoxide) or a weak base (e.g., a carboxylate). Exemplary amine or amide compounds include amines such as Troger's base, hindered amines such as diazabicycloundecene (DBU) and diazabicyclononene (DBN), N-protected amines such as N-t-butylcarbonyl-1,1-bis(hydroxymethyl)-2-hydroxyethylamine, and ionic compounds including quaternary alkyl ammonium salts such as tetrabutylammonium hydroxide (TBAH) and tetrabutyl ammonium lactate.

Examples of photo-destroyable quenchers include triphenylsulfonium hydroxide, triphenylsulfonium 3-hydroxyadamantane carboxylate, triphenylsulfonium camphorsulfonate, and t-butylphenyldibenzothiophenium 1-adamantanecarboxylate.

Solvents generally suitable for dissolving, dispensing, and coating the components include anisole; esters including ethyl lactate, methyl 2-hydroxybutyrate (HBM), n-butyl acetate, 1-methoxy-2-propyl acetate (also referred to as propylene glycol methyl ether acetate, PGMEA), methoxyethyl propionate, ethoxyethyl propionate, and gamma-butyrolactone; alcohols including 1-methoxy-2-propanol (also referred to as propylene glycol methyl ether, PGME), and 1-ethoxy-2 propanol; ketones including cyclohexanone and 2-heptanone; and combinations thereof.

Surfactants include fluorinated and non-fluorinated surfactants, and are preferably non-ionic. Exemplary fluorinated non-ionic surfactants include perfluoro C₄ surfactants such as FC-4430 and FC-4432 surfactants, available from 3M Corporation; and fluorodiols such as POLYFOX™ PF-636, PF-6320, PF-656, and PF-6520 fluorosurfactants from Omnova.

In a very specific embodiment of the photoresist composition, each of the photoacid-generating repeat units of the first polymer has the structure

wherein R³ is independently in each of the photoacid-generating repeat units hydrogen or methyl; L² is —O— in each of the photoacid-generating repeat units; L³ is independently in each of the photoacid-generating repeat units an unsubstituted or substituted C₁₋₂₀ hydrocarbylene, wherein the substituted C₁₋₂₀ hydrocarbylene can, optionally, comprise one or more in-chain divalent heteroatom-containing groups that is —O—, —OC(O)—, or —C(O)O—; and q is independently in each of the photoacid-generating repeat units 1, 2, 3, 4, or 5; r is zero at each occurrence in each of the photoacid-generating repeat units; at least one occurrence of R¹ in each of the photoacid-generating repeat units comprises a tertiary carboxylic acid ester, an acetal, or a ketal; m is 1 in each of the photoacid-generating repeat units; and X is a single bond in each of the photoacid-generating repeat units; and the second polymer comprises 10 to 65 mole percent of acid-labile repeat units, 0 to 50 weight percent of base-labile repeat units, 0 to 40 mole percent of base-soluble repeat units, and 0 to 15 mole percent of photoacid-generating repeat units; and the photoresist composition comprises, on a dry weight basis, 20 to 80 weight percent of the first polymer, 10 to 60 weight percent of the second polymer, and 0.5 to 10 weight percent of a quencher.

The photoresist composition can be used to form a film comprising the photoresist, where the film on the substrate constitutes a coated substrate. Such a coated substrate includes: (a) a substrate having one or more layers to be patterned on a surface thereof; and (b) a layer of the photoresist composition over the one or more layers to be patterned. Preferably, patterning is carried out using ultraviolet radiation at wavelength of less than 248 nm, and in particular, at 193 nm or 13.4 nm. A method of forming an electronic device includes: (a) applying a layer of the photoresist composition on a substrate; (b) pattern-wise exposing the photoresist composition layer to activating radiation; and (c) developing the exposed photoresist composition layer to provide a resist relief image. In some embodiments, the radiation is ultraviolet (UV), extreme ultraviolet (EUV) or electron beam (e-beam) radiation.

Developing the pattern can be accomplished by either positive tone development (PTD) in which the pattern-wise exposed region is removed by the action of an aqueous base developer such as aqueous tetramethylammonium hydroxide (TMAH). An exemplary positive tone developer is 0.26 Normal aqueous TMAH. Alternatively, the same pattern-wise exposure can be developed using an organic solvent developer to provide a negative tone development (NTD) in which the unexposed region of a pattern is removed by the action of a negative tone developer. Useful solvents for negative tone development include those also useful for dissolving, dispensing, and coating. Exemplary negative tone developer solvents include propylene glycol methyl ether acetate (PGMEA), methyl 2-hydroxyisobutyrate (HBM), n-butyl acetate, methoxyethyl propionate, ethoxyethyl propionate, and gamma-butyrolactone, cyclohexanone, 2-heptanone, and combinations thereof. A method of making a pattern thus includes pattern-wise exposing a photoresist composition layer with actinic radiation, and developing the pattern by treatment with an aqueous alkaline developer to form a positive tone relief image, or with an organic solvent developer to form a negative tone relief image.

Substrates can be any dimension and shape, and are preferably those useful for photolithography, such as silicon, silicon dioxide, silicon-on-insulator (SOI), strained silicon, gallium arsenide, coated substrates including those coated with silicon nitride, silicon oxynitride, titanium nitride, tantalum nitride, ultrathin gate oxides such as hafnium oxide, metal or metal coated substrates including those coated with titanium, tantalum, copper, aluminum, tungsten, alloys thereof, and combinations thereof. The surfaces of substrates herein can include critical dimension layers to be patterned including, for example, one or more gate-level layers or other critical dimension layer on the substrates for semiconductor manufacture. The substrates can be formed as circular wafers having dimensions such as, for example, 200 millimeters, 300 millimeters, or larger in diameter, or other dimensions useful for wafer fabrication.

The invention is further illustrated by the following non-limiting examples.

Example 1

FIG. 1 is a synthetic scheme for the preparation of 5-(3,5-dimethyl-4-(2-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-2-oxoethoxy)phenyl)-5H-dibenzo[b,d]thiophen-5-ium ((1S,4S)-7,7-dimethyl-2-oxobicyclo[2.2.1]heptan-1-yl)methanesulfonate.

5-(3,5-Dimethyl-4-(2-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-2-oxoethoxy)phenyl)-5H-dibenzo[b,d]thiophen-5-ium 41S,4S)-7,7-dimethyl-2-oxobicyclo[2.2.1]heptan-1-yl)methanesulfonate

5-(3,5-dimethyl-4-(2-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-2-oxoethoxy)phenyl)-5H-dibenzo[b,d]thiophen-5-ium ((1S,4S)-7,7-dimethyl-2-oxobicyclo[2.2.1]heptan-1-yl)methanesulfonate chloride (19.4 g, 35.6 mmol) and sodium camphorsulfonate (9.52 g, 37.4 mmol) were dissolved in dichloromethane (200 mL) and water (200 mL) and stirred at room temperature overnight. The layers were separated and the organic phase washed with water (6×150 mL) and concentrated. The crude solid was dissolved in minimal dichloromethane, precipitated into methyl tert-butyl ether (500 mL), filtered and dried to afford the title compound (19.0 g, 72%) as a white solid. ¹H NMR (500 MHz, (CD₃)₂CO) δ: 8.52 (d, J=7.8 Hz, 2H), 8.33 (d, J=7.8 Hz, 2H), 7.97 (dt, J=8.4, 0.9 Hz, 2H), 7.76 (dt, J=8.1, 0.9 Hz, 2H), 7.32 (s, 2H), 4.56 (s, 2H), 2.86 (d, J=17.7 Hz, 1H), 2.72 (t, J=7.5 Hz, 1H), 2.35 (d, J=17.7 Hz, 1H), 2.22 (s, 6H), 2.13-2.28 (m, 2H), 1.44-1.97 (m, 26H), 1.26 (d, J=9 Hz, 1H).

Example 2

FIG. 2 is a synthetic scheme for the preparation of 2-(2-methoxyethoxy)ethyl 4-tosylate.

2-(2-Methoxyethoxy)ethyl 4-tosylate

Sodium hydroxide (62 g, 1.55 mol) in water (350 mL) was carefully added in one portion to 2-(2-methoxyethoxy)ethanol (110 g, 912 mmol) in tetrahydrofuran (350 mL) at 0° C. under vigorous stirring and stirred for 5 min. Then tosyl chloride (209 g, 1.09 mol) in tetrahydrofuran (350 mL) was added over 10 minutes, warmed to room temperature and stirred for 4 hours. The reaction mixture was diluted with water (350 mL) and extracted with methyl tert-butyl ether (2×700 mL). The combined organic layers were washed with 1M aqueous sodium hydroxide (2×500 mL), water (3×500 mL), dried over sodium sulfonate and concentrated to afford the title compound (221 g, 88%) as a clear oil. ¹H NMR (500 MHz, (CD₃)₂CO) δ: 7.81 (d, J=8.0 Hz, 2H), 7.49 (d, J=8.0 Hz, 2H), 4.14-4.19 (m, 2H), 3.63-3.68 (m, 2H), 3.49-3.53 (m, 2H), 3.39-3.44 (m, 2H), 3.26 (s, 3H), 3.47 (s, 3H).

Example 3

FIG. 3 is a synthetic scheme for the preparation of 2-(2-(2-methoxyethoxy)ethoxy)-1,3-dimethylbenzene.

2-(2-(2-Methoxyethoxy)ethoxy)-1,3-dimethylbenzene

Dimethylformamide (200 mL) was added to sodium hydride (18 g as 60 weight percent in oil, 450 mmol) under nitrogen. Next, 2,6-dimethylphenol (50 g, 409 mmol) in dimethylformamide (100 mL) was added drop-wise and heated to 50° C. where 2-(2-methoxyethoxy)ethyl 4-tosylate (113 g, 413 mmol) in dimethylformamide (200 mL) was added drop-wise and stirred overnight. The reaction mixture was diluted with methyl tert-butyl ether (1 L) and washed with water (1 L). The water layer was back extracted with methyl tert-butyl ether (500 mL) and the combined organics washed with 1M potassium hydroxide (3×300 mL), hydrochloric acid (1 weight percent, 2×500 mL), water (2×500 mL), brine (1×250 mL), dried over sodium sulfate and concentrated to afford the title compound (90.5 g, 90%) as a clear oil. ¹H NMR (300 MHz, (CD₃)₂CO) δ : 6.99 (d, J=7.8 Hz, 2H), 6.88 (t, J=7.8 Hz, 1H), 3.90-3.94 (m, 2H), 3.75-3.80 (m, 2H), 3.64-3.68 (m, 2H), 3.50-3.54 (m, 2H), 3.31 (s, 3H), 2.26 (s, 6H).

Example 4

FIG. 4 is a synthetic scheme for the preparation of 5-(4-(2-(2-methoxyethoxy)ethoxy)-3,5-dimethylphenyl)-dibenzothiophen-5-ium iodide.

5-(4-(2-(2-Methoxyethoxy)ethoxy)-3,5-dimethylphenyl)-dibenzothiophen-5-ium iodide

Eaton's Reagent (60 mL) was added to a solution of dibenzothiophene oxide (20.0 g, 0.1 mol) and 2-(2-(2-methoxyethoxy)ethoxy)-1,3-dimethylbenzene (24.7 g, 0.11 mol) in dichloromethane (60 mL) at 0° C., warmed to room temperature and stirred overnight. The reaction mixture was cooled to 0° C. and slowly quenched by the addition of water (300 mL) and washed with methyl tert-butyl ether (2×250 mL). The organic layer is discarded and sodium iodide (30 g, 0.200 mmol) in water (100 mL) was added to the aqueous layer under vigorous stirring. The precipitate was filtered and washed with copious amounts of water, suspended in minimal acetone, stirred at room temperature for 1 hour and filtered to afford the title compound (30.2 g, 57%) as an off-white solid. ¹H NMR (500 MHz, (CD₃)₂SO) δ : 8.52 (d, J=8.0 Hz, 2H), 8.33 (d, J=8.0 Hz, 2H), 7.96 (t, J=7.5 Hz, 2H), 7.75 (d, J=7.5 Hz, 2H), 7.31 (s, 2H), 3.94 (vis t, J=5.5 Hz, 2H), 3.67 (vis t, J=5.0 Hz, 2H), 3.55 (vis t, 6.0 Hz, 2H), 3.42 (vis t, J=4.5 Hz, 2H), 3.21 (s, 3H), 2.20 (s, 6H).

Example 5

FIG. 5 is a synthetic scheme for the preparation of 5-(4-(2-(2-methoxyethoxy)ethoxy)-3,5-dimethylphenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate.

5-(4-(2-(2-Methoxyethoxy)ethoxy)-3,5-dimethylphenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate

5-(4-(2-(2-methoxyethoxy)ethoxy)-3,5-dimethylphenyl)-dibenzothiophen-5-ium iodide (13.0 g, 24.3 mmol) and triethylammonium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate (8.22 g, 24.8 mmol) were dissolved in dichloromethane (150 mL) and water (150 mL) and stirred at room temperature overnight. The layers were separated and the organic layer was washed with water (8×150 mL) and concentrated under reduced pressure to afford the title compound (15.1 g, 97%) as a white hydroscopic solid which was stored under inert nitrogen atmosphere. ¹H NMR (500 MHz, (CD₃)₂CO) δ : 8.52 (d, J=8.0 Hz, 2H), 8.38 (d, J=8.5 Hz, 2H), 8.00 (t, J=7.5 Hz, 2H), 7.80 (t, J=8.0 Hz, 2H), 7.51 (s, 2H), 6.13-6.16 (m, 1H), 5.67-5.69 (m, 1H), 4.77 t, J=15.5 Hz, 2H), 4.02-4.05 (m, 2H0, 3.73-3.77 (m, 2H), 3.58-3.62 (m, 2H), 3.44-3.49 (m, 2H), 3.25 (s, 3H), 2.26 (s, 6H), 1.13 (s, 3H).

Example 6

FIG. 6 is a synthetic scheme for the preparation of 5-(4-methoxy-3-(4-((2-methyladamantan-2-yl)oxy)-1-(2-((2-methyladamantan-2-yl)oxy)-2-oxoethoxy)-1,4-dioxobutan-2-yl)phenyl)-dibenzothiophenium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate.

5-(4-Methoxy-3-(4-((2-methyladamantan-2-yl)oxy)-1-(2-((2-methyladamantan-2-yl)oxy)-2-oxoethoxy)-1,4-dioxobutan-2-yl)phenyl)-dibenzothiophenium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate

5-(4-methoxy-3-(4-((2-methyladamantan-2-yl)oxy)-1-(2-((2-methyladamantan-2-yl)oxy)-2-oxoethoxy)-1,4-dioxobutan-2-yl)phenyl)-dibenzothiophenium chloride (37.8 g, 47.4 mmol and N,N,N-trimethyl-1-phenylmethanaminium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate (18.9 g, 49.8 mmol) were dissolved in DCM (250 mL) and water (250 mL) and stirred at 25° C. overnight. The layers were separated, the aqueous phase extracted with dichloromethane (100 mL), the combined organic layers washed with water (8×200 mL) and concentrated under reduced pressure to afford the title compound (36.0, 77%) as an off white solid. ¹H NMR (500 MHz, (CD₃)₂CO) δ: (8.52-8.56 (m, 2H), 8.37 (d, J=8 Hz, 1H), 8.31 (d, J=8.5 Hz, 1H), 7.99-8.06 (m, 2H), 7.78-7.85 (m, 3H), 7.63 (dd, J=9, 1.5 Hz, 1H), 7.31 (d, J=9 Hz, 1H), 6.16-6.19 (m, 1H), 5.64-6.69 (m, 1H), 5.62 (s, 2h), 4.72-4.79 (m, 2H), 4.50-4.65 (m, 2H), 4.42-4.47 (m, 1H), 3.96 (s, 3H), 2.99-3.07 (m, 1H), 2.63-2.70 (m, 1H), 2.10-2.30 (m, 4H), (1.42-2.09 (m, 31H).

Example 7

FIG. 7 is a synthetic scheme for the preparation of 5-(4-methoxy-3-(4-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-1-(2-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-2-oxoethoxy)-1,4-dioxobutan-2-yl)phenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(2-(methacryloyloxy)acetoxy)ethanesulfonate.

5-(4-Methoxy-3-(4-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-1-(2-(41R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-2-oxoethoxy)-1,4-dioxobutan-2-yl)phenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(2-(methacryloyloxy)acetoxy)ethanesulfonate

5-(4-methoxy-3-(4-((2-methyladamantan-2-yl)oxy)-1-(2-((2-methyladamantan-2-yl)oxy)-2-oxoethoxy)-1,4-dioxobutan-2-yl)phenyl)-dibenzothiophenium chloride (40.0 g, 50.2 mmol) and N,N,N-trimethyl-1-phenylmethanaminium 1,1-difluoro-2-(2-(methacryloyloxy)acetoxy)ethanesulfonate (23.0 g, 52.6 mmol) were dissolved in dichloromethane (300 mL) and water (300 mL) and stirred at room temperature overnight. The layers were separated, the organic phase washed with water (7×250 mL) and concentrated to afford the title compound (43.4 g, 83%) as a white solid. ¹H NMR (300 MHz, (CD₃)₂SO) δ : 8.52 (d, J=7.8 Hz, 2H), 8.31 (d, J=8.1 Hz, 1H), 8.26 (d, J=8.1 Hz, 1H), 7.97 (t, J=7.8 Hz, 2H), 7.75 (t, J=7.8 Hz, 2H), 7.71 (d, J=2.4 Hz, 1H), 7.35 (dd, J=9.0, 2.4 Hz, 1H), 7.22 (d, J=9.0 Hz, 1H), 6.12-6.17 (m, 1H), 5.76-5.82 (m, 1H), 4.87 (s, 2H), 4.63 (t, J=15.6 Hz, 2H), 4.59 (s, 2H), 4.35 (t, J=7.5 Hz, 1H), 3.82 (s, 3H), 2.92-3.10 (m, 2H), 2.56-2.68 (m, 1H), 1.35-2.25 (m, 36H).

Example 8

FIG. 8 is a synthetic scheme for the preparation of 5-(4-methoxy-3-(2-(2-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-2-oxoethoxy)-2-oxo-1-(2-oxotetrahydrofuran-3-yl)ethyl)phenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate.

5-(4-Methoxy-3-(2-(2-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-2-oxoethoxy)-2-oxo-1-(2-oxotetrahydrofuran-3-yl)ethyl)phenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate

5-(4-methoxy-3-(2-(2-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-2-oxoethoxy)-2-oxo-1-(2-oxotetrahydrofuran-3-yl)ethyl)phenyl)-5H-dibenzo[b,d]thiophen-5-ium chloride (40.0 g, 59.2 mmol) and N,N,N-trimethyl-1-phenylmethanaminium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate (23.6 g, 62.2 mmol) were dissolved in dichloromethane (300 mL) and water (300 mL) and stirred at room temperature overnight. The layers were separated, the organic phase washed with water (7×250 mL), concentrated to half volume and precipitated into methyl tert-butyl ether (1.5 L). The precipitate was filtered, washed with methyl tert-butyl ether (2×500 mL) and dried to afford the title compound (39.1 g, 76%) as a white solid. ¹H NMR (300 MHz, (CD₃)₂SO) δ : 8.53 (d, J=7.8 Hz, 2H), 8.34 (d, J=8.1 Hz, 2H), 8.27 (d, J=7.8 Hz, 2H), 7.97 (t, J=7.5 Hz, 2H), 7.75 (dt, J=7.8, 2.7 Hz, 1H), 7.68 (d, J=1.8 Hz, 1H), 7.38 (dd, J=9.0, 2.1 Hz, 1H), 7.23 (d, J=9.0 Hz, 1H), 6.12 (vis s, 1H), 5.77 (vis s, 1H), 4.64 (t, J=15.6 Hz, 2H), 4.60 (s, 2H), 4.25 (d, J=7.2 Hz, 1H), 4.05-4.21 (m, 2H), 3.82 (s, 3H), 3.36-3.51 (m, 2H), 2.14-2.20 (m, 1H), 1.38-2.04 (m, 17H).

Example 9

In general polymer molecular weight were determined from ¹³C NMR spectra obtained on a Varian 300 Megahertz NMR spectrometer operating with a relaxation delay of 2 seconds by integration of initiator end groups and one of the carbons of the PAG unit.

FIG. 9 is a synthetic scheme for the preparation of a homopolymer of 5-(4-methoxy-3-(4-((2-methyladamantan-2-yl)oxy)-1-(2-((2-methyladamantan-2-yl)oxy)-2-oxoethoxy)-1,4-dioxobutan-2-yl)phenyl)-dibenzothiophenium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate.

Homopolymer of 5-(4-methoxy-3-(4-((2-methyladamantan-2-yl)oxy)-1-(2-((2-methyladamantan-2-yl)oxy)-2-oxoethoxy)-1,4-dioxobutan-2-yl)phenyl)-dibenzothiophenium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate

5-(4-methoxy-3-(4-((2-methyladamantan-2-yl)oxy)-1-(2-((2-methyladamantan-2-yl)oxy)-2-oxoethoxy)-1,4-dioxobutan-2-yl)phenyl)-dibenzothiophenium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate (10.0 g, 10.2 mmol) was dissolved in ethyl lactate/gamma-butyrolactone (3/7 v/v, 15.0 g). The initiator 2,2′-azobis(2.4-dimethyl valeronitrile) (1.00 g) was dissolved in acetonitrile/tetrahydrofuran (2/1 v/v, 1.00 g). The monomer and initiator solutions were added drop-wise over 4 hours to a flask preheated to 80° C. followed by an initiator chase. The reaction mixture was stirred for 2 hours, cooled to room temperature, diluted with methanol (17 g) and precipitated into diisopropyl ether (800 g). The polymer was filtered and dried to afford the title compound (8.00 g, 80%, weight average molecular weight 3972) as a white solid.

Example 10

FIG. 10 is a synthetic scheme for the preparation of a homopolymer of 5-(4-methoxy-3-(4-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-1-(2-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-2-oxoethoxy)-1,4-dioxobutan-2-yl)phenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(2-(methacryloyloxy)acetoxy)ethanesulfonate.

Homopolymer of 5-(4-methoxy-3-(4-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-1-(2-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-2-oxoethoxy)-1,4-dioxobutan-2-yl)phenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(2-(methacryloyloxy)acetoxy)ethanesulfonate. 5-(4-methoxy-3-(4-((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-1-(2-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-2-oxoethoxy)-1,4-dioxobutan-2-yl)phenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(2-(methacryloyloxy)acetoxy)ethanesulfonate (1.00 g, 0.953 mmol) was dissolved in ethyl lactate/gamma-butyrolactone (3/7 v/v, 1.50 g). 2,2′-Azobis(2.4-dimethyl valeronitrile) (0.150 g) was dissolved in acetonitrile/tetrahydrofuran (2/1 v/v, 0.150 g). The monomer and initiator solutions were added drop-wise to a flask preheated to 75° C. and stirred for 8 h. The reaction mixture was cooled to room temperature, diluted with acetone (0.900 g) and precipitated as a sticky solid from acetone/diisopropyl ether (1:1 25.0 g), decanted, redissolved in acetone (2.40 g) and methanol (0.500 g) and precipitated into diisopropyl ether (20× reaction volume). The polymer was filtered and dried to afford the title compound (0.550 g, 55%, weight average molecular weight 3,000 daltons) as a white solid.

Example 11

FIG. 11 is a synthetic scheme for the preparation of a homopolymer of 5-(4-methoxy-3-(2-(2-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-2-oxoethoxy)-2-oxo-1-(2-oxotetrahydrofuran-3-yl)ethyl)phenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate.

Homopolymer of 5-(4-methoxy-3-(2-(2-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-2-oxoethoxy)-2-oxo-1-(2-oxotetrahydrofuran-3-yl)ethyl)phenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate

5-(4-methoxy-3-(2-(2-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-2-oxoethoxy)-2-oxo-1-(2-oxotetrahydrofuran-3-yl)ethyl)phenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate (15.0 g, 17.3 mmol) was dissolved in ethyl lactate/gamma-butyrolactone (3/7 v/v, 60.0 g). 2,2′-Azobis(2.4-dimethyl valeronitrile) (2.25 g) was dissolved in acetonitrile/tetrahydrofuran (2/1 v/v, 2.25 g). The monomer and initiator solutions were added drop-wise over 4 hours to a flask preheated to 90° C. The reaction mixture was cooled to room temperature, diluted with tetrahydrofuran (10× reaction volume) and acetone (5× reaction volume) and precipitated into diisopropyl ether (2000 g). The polymer was filtered and dried to afford the title compound (7.96 g, 53%, weight average molecular weight 3,476 daltons) as a white solid.

Example 12

FIG. 12 is a synthetic scheme for the preparation of a copolymer of 5-(4-(2-(2-methoxyethoxy)ethoxy)-3,5-dimethylphenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate and 5-(4-methoxy-3-(4-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-1-(2-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-2-oxoethoxy)-1,4-dioxobutan-2-yl)phenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(2-(methacryloyloxy)acetoxy)ethanesulfonate.

Copolymer of 5-(4-(2-(2-methoxyethoxy)ethoxy)-3,5-dimethylphenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate and 5-(4-methoxy-3-(4-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-1-(2-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-2-oxoethoxy)-1,4-dioxobutan-2-yl)phenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(2-(methacryloyloxy)acetoxy)ethanesulfonate

5-(4-(2-(2-methoxyethoxy)ethoxy)-3,5-dimethylphenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate (3.00 g, 8.25 mmol) and 5-(4-methoxy-3-(4-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-1-(2-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-2-oxoethoxy)-1,4-dioxobutan-2-yl)phenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(2-(methacryloyloxy)acetoxy)ethanesulfonate (7.00 g, 6.67 mmol) were dissolved in ethyl lactate/gamma-butyrolactone (3/7 v/v, 15.0 g). 2,2′-Azobis(2.4-dimethyl valeronitrile) (1.50 g) was dissolved in acetonitrile/tetrahydrofuran (2/1 v/v, 1.50 g). The monomer and initiator solutions were added drop-wise to a flask preheated to 75° C. over 4 hours. The reaction mixture was cooled to room temperature, precipitated as a sticky solid from methanol/diisopropyl ether (1:1, 20× reaction volume), redissolved into acetone (20.0 mL) and methanol (0.300 g) and reprecipitated from diisopropyl ether/methanol (19:1 v/v, 2,000 mL), filtered and dried to afford the title compound (6.00 g, 60%, weight average molecular weight 2,500) as a white solid.

Example 13

FIG. 13 is a synthetic scheme for the preparation of a copolymer 5-(4-(2-(2-methoxyethoxy)ethoxy)-3,5-dimethylphenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate and 5-(4-methoxy-3-(2-(2-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-2-oxoethoxy)-2-oxo-1-(2-oxotetrahydrofuran-3-yl)ethyl)phenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate.

Copolymer 5-(4-(2-(2-methoxyethoxy)ethoxy)-3,5-dimethylphenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate and 5-(4-methoxy-3-(2-(2-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-2-oxoethoxy)-2-oxo-1-(2-oxotetrahydrofuran-3-yl)ethyl)phenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate

5-(4-(2-(2-methoxyethoxy)ethoxy)-3,5-dimethylphenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate (4.50 g, 12.4 mmol) and 5-(4-methoxy-3-(2-(2-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-2-oxoethoxy)-2-oxo-1-(2-oxotetrahydrofuran-3-yl)ethyl)phenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate (10.5 g, 12.1 mmol) were dissolved in ethyl lactate/gamma-butyrolactone (3/7 v/v, 60.0 g). 2,2′-Azobis(2.4-dimethyl valeronitrile) (2.25 g) was dissolved in acetonitrile/tetrahydrofuran (2/1 v/v, 2.25 g). The monomer and initiator solutions were added drop-wise to a flask preheated to 75° C. over 4 h. The reaction mixture was cooled to room temperature, diluted with tetrahydrofuran (5× reaction volume) and acetone (5× reaction volume), precipitated from diisopropyl ether (20× reaction volume), filtered and dried to afford the title compound (11.0 g, 73%, weight average molecular weight 2,700 daltons) as a white solid.

Example 14 Preparation of Tetrapolymer with Acid Generator Units

A heel solution was made by dissolving 2-phenylpropan-2-ylmethacrylate (0.39 g), 2-oxotetrahydrofuran-3-yl methacrylate (0.33 g), 3,5-bis(1,1,1,3,3,3-hexafluoro-2-hydroxypropan-2-yl)cyclohexyl methacrylate (0.57 g) and 5-(4-(2-(1-ethylcyclopentyloxy)-2-oxoethoxy)-3,5-dimethylphenyl)-5H-dibenzo[b,d]thiophenium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate (0.31 g) in 12.81 g ethyl lactate/gamma-butyrolactone (7/3 v/v). Feed solution was prepared by dissolving 2-phenylpropan-2-yl methacrylate (185.54 g, 0.967 mol), 2-oxotetrahydrofuran-3-yl methacrylate (204.27 g, 1.26 mol), 3,5-bis(1,1,1,3,3,3-hexafluoro-2-hydroxypropan-2-yl)cyclohexyl methacrylate (127.98 g, 0.29 mol) and 5-(4-(2-(1-ethylcyclopentyloxy)-2-oxoethoxy)-3,5-dimethylphenyl)-5H-dibenzo[b,d]thiophenium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate (81.5 g, 0.132 mol) in 606 g ethyl lactate: gamma-butyrolactone (30/70 v/v). Initiator solution was prepared by dissolving 65.96 g initiator (2,2′-azobis(2,4-dimethyl valeronitrile)) in 66 g acetonitrile/tetrahydrofuran (2/1 v/v). The polymerization was carried out in a 2 L 3-neck round bottom flask fitted with a water condenser and a thermometer to monitor the reaction in the flask. The contents were stirred using an overhead stirrer. The reactor was charged with the heel solution and the contents were heated to 75° C. The feed solution and the initiator solution were fed into the reactor using syringe pump over a 4 hour time period. The contents were then stirred for additional 2 hours, whereby, the reaction was quenched using hydroquinone (2.0 g). The contents were cooled to room temperature and precipitated twice out of 10× (by weight) diisopropyl ether/methanol 95/5 (w/w). The polymer obtained was dried under vacuum after each precipitation step at 50° C. for 24 hours to yield 500 g polymer having a weight average molecular weight of 5,200 daltons, a dispersity of 1.5, and a monomer composition of the respective monomers of 36.0 mole percent, 47.5 mole percent, 11.0 mole percent, and 5.5 mole percent.

Example 15 Preparation of Tetrapolymer with Acid Generator Units

The process of Example 14 was repeated, except that equimolar 5-phenyl-5H-dibenzo[b,d]thiophenium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate was used in place of 5-(4-(2-(1-ethylcyclopentyloxy)-2-oxoethoxy)-3,5-dimethylphenyl)-5H-dibenzo[b,d]thiophenium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate. The polymer obtained had a weight average molecular weight of 6,300 daltons, a dispersity of 1.4, and respective monomer contents of 36.5 mole percent, 47.5 mole percent, 12.0 mole percent, and 5 mole percent.

Example 16 Preparation of Tetrapolymer with Acid Generator Units (TBPPDBTS-F2)

The process of Example 14 was repeated, except that equimolar 5-(4-(tert-butyl)phenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate was used in place of 5-(4-(2-(1-ethylcyclopentyloxy)-2-oxoethoxy)-3,5-dimethylphenyl)-5H-dibenzo[b,d]thiophenium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate. The polymer obtained had a weight average molecular weight of 5,200 daltons, a dispersity of 1.6, and respective monomer contents of 34 mole percent, 51 mole percent, 9 mole percent, and 6 mole percent.

Example 17 Preparation of Tetrapolymer with Acid Generator Units

The process of Example 14 was repeated, except that an equimolar amount of the monomer of Example 9 was used in place of 5-(4-(2-(1-ethylcyclopentyloxy)-2-oxoethoxy)-3,5-dimethylphenyl)-5H-dibenzo[b,d]thiophenium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate. The polymer obtained had a weight average molecular weight of 5,200 daltons, a dispersity of 1.5, and respective monomer contents of 38 mole percent, 46 mole percent, 10 mole percent, and 6 mole percent.

Example 18 Preparation of Terpolymer without Acid Generator Units

Heel solution was made by dissolving 2-phenylpropan-2-ylmethacrylate (1.94 g), 2-oxotetrahydrofuran-3-yl methacrylate (1.7 g), 3,5-bis(1,1,1,3,3,3-hexafluoro-2-hydroxypropan-2-yl)cyclohexyl methacrylate (2.81 g) in 72 g ethyl lactate:gamma-butyrolactone (30/70 v/v). Feed solution was prepared by dissolving 2-phenylpropan-2-yl methacrylate (33.08 g), 2-oxotetrahydrofuran-3-yl methacrylate (35.97 g), 3,5-bis(1,1,1,3,3,3-hexafluoro-2-hydroxypropan-2-yl)cyclohexyl methacrylate (23.91 g) in 94 g ethyl lactate: gamma-butyrolactone (30/70 v/v). Initiator solution was prepared by dissolving 11 g initiator (2,2′-azobis(2,4-dimethyl valeronitrile)) in 11 g acetonitrile/tetrahydrofuran (2/1 v/v). The polymerization was carried out in a 2 L 3-neck round bottom flask fitted with a water condenser and a thermometer to monitor the reaction in the flask. The contents were stirred using an overhead stirrer. The reactor was charged with the heel solution and the contents were heated to 75° C. The feed solution and the initiator solution were fed into the reactor using syringe pumps over a 4 hour time period. The contents were then stirred for additional 2 hours, after which the reaction was quenched using hydroquinone (1.0 g). The contents were cooled to room temperature and precipitated twice out of 10× (by weight) isopropyl ether/methanol 95/5 (w/w). The polymer obtained was dried under vacuum after each precipitation step at 50° C. for 24 hours to yield 100 g polymer having a weight average molecular weight of 5,000 daltons, a dispersity of 1.5, and respective monomer contents of 43 mole percent, 46 mole percent, and 11 mole percent.

Example 19 Preparation and Processing of a Photoresist Composition

Non-polymeric photoacid generators and photo-destroyable quenchers (collectively, “additives”) used in the preparation of photoresist compositions are summarized in Table 1. Photoresist compositions are summarized in Table 2. The Example 19 positive-tone photoresist composition was prepared by combining component 1, 5.33 g of a 10 weight percent solution of the polymer of Example 17 in ethyl lactate; component 2, 10.373 g of a 2 weight percent solution of the additive A-1 in ethyl lactate; component 3, 0.320 g of a 0.5 weight percent solution of tetrakis(2-hydroxypropyl)ethylenediamine in ethyl lactate; component 4, 0.356 g of a 2 weight percent solution of the additive A-2 in ethyl lactate; component 5, 0.107 g of a 0.5 weight percent solution of fluorinated surfactant (Omnova PF656) in ethyl lactate; component 6, 4.737 g of ethyl lactate; and component 7, 8.775 g of 2-hydroxyisobutyric acid methyl ester. The formulated resist was passed through a 0.01 micrometer (μm) polytetrafluoroethylene (PTFE) filter. The thus prepared resist was spin coated onto a silicon wafer, soft baked to remove carrier solvent and exposed through a photomask to EUV radiation. The imaged resist layer was then baked at 110° C. for 60 seconds and then developed with an aqueous alkaline composition.

TABLE 1 Additive Structure A-1

A-2

A-3

A-4

A-5

A-6

A-7

For Table 2, below, components 1-7 correspond to the descriptions in Example 19. Component amounts, in brackets, are expressed in units of grams.

TABLE 2 Comp. 1 Comp. 2 Comp. 3 Comp. 4 Comp. 5 Comp. 6 Comp. 7 Ex. polymer PAG/polyPAG quencher PDQ surfactant solvent solvent 19 Ex. 17 A-1 [0.320] A-2 [0.107] [4.737] [8.775] (C) [5.330] [10.37] [0.356] 20 Ex. 16 A-1 [0.563] A-2 [0.188] [9.826] [14.63] (C) [9.378] [14.79] [0.626] 21 Ex. 15 — [0.478] — [0.318] [25.76] [17.52] (C) [15.92] 22 Ex. 14 A-3 [13.30] — [1.109] [48.17] [87.75] (C) [55.4] [94.24] 23 Ex. 18 A-4 [1.443] — [0.126] [12.23] [11.76] (C) [6.292] [8.148] 24 Ex. 18 A-5 [0.954]* — [0.146] [13.61] [14.70] (C) [7.283] [13.31] 25 Ex. 18 A-6 [0.846]* — [0.129] [10.40] [14.70] (C) [6.458] [17.47] 26 Ex. 14 Ex. 9 [2.120] — [0.177] [6.570] [14.63] (I) [8.850] [17.64] 27 Ex. 14 Ex. 9 [0.618] A-7 [0.105] [4.271] [8.775] (I) [5.272] [10.507] [0.451] 28 Ex. 16 Ex. 9 [1.308] — [0.114] [9.974] [11.76] (I) [5.700] [11.14] 29 Ex. 18 Ex. 9 [1.308] — [0.114] [9.974] [11.76] (I) [5.700] [11.14] 30 Ex. 16 — [0.239] — [0.160] [19.861] [11.76] (C) [7.980] *Triisopropanolamine

Critical Dimension Uniformity

Critical dimension uniformity (CDU) is the calculated 3 Sigma (three standard deviations) for ten Fields of View (FOV) measuring 36 contact holes for each FOV, all taken at Best Exposure/Best Focus. Each data point has been pre-normalized to a standard EUV photoresist which is run in each lithographic slot to eliminate variability and noise. The results, presented in Tables 3 and 4, show that the lowest (best) CDU values are exhibited by the inventive Examples 26 and 27 photoresists with polymer comprising 50 to 100 mole percent of photoacid-generating repeat units. These inventive examples outperformed comparative examples with polymers having less than 50 mole percent of photoacid-generating repeat units, with or without non-polymer-bound photoacid generator. In Tables 3 and 4, the CDU of Examples 26 and 27 are normalized to 1, and designated with “0”. Comparative examples which underperform relative to the example by 0-15% are designated with“”; comparative examples which underperform relative to the example by 15-35% are designated with “▪”; and comparative examples which underperform relative to the example by >35% are designated with “□”. In Table 3, “PolyPAG” refers to a polymer comprising 50 to 100 mole percent of photoacid-generating repeat units, “Polymer-bound-PAG” refers to a polymer comprising photoacid-generating repeat units in an amount less than 50 mole percent, and “free PAG” refers to a non-polymer-bound photoacid-generator.

TABLE 3 CDU Example PAG Type Normalized Example 26 PolyPAG + Polymer-bound-PAG ⋄ Comparative Polymer-bound-PAG + free PAG ▪ Example 19 Comparative Polymer-bound-PAG + free PAG □ Example 20 Comparative Polymer-bound-PAG □ Example 21 Comparative Polymer-bound-PAG + free PAG ▪ Example 22

TABLE 4 CDU Example PAG Type Normalized Example 27 PolyPAG + Polymer-bound-PAG ⋄ Comparative Polymer-bound-PAG + free PAG  Example 19 Comparative Polymer-bound-PAG + free PAG ▪ Example 20 Comparative Polymer-bound-PAG ▪ Example 21 Comparative Polymer-bound-PAG + free PAG  Example 22

Contact Hole Exposure Latitude

Exposure latitude % (EL %) were calculated from critical dimension (CD) data through dose and focus (FEM) with 10% CD boundaries restricted to 100 nm depth of focus (DoF) for 30 nm contact holes at 1:1 half pitch. The results, presented in Table 5, show that the largest (best) exposure latitude is exhibited by the inventive Example 26, which contains a polymer comprising 50 to 100 mole percent of photoacid-generating repeat units in combination with a polymer having less than 50 mole percent of photoacid-generating repeat units. This inventive example outperformed comparative examples with polymers having less than 50 mole percent of photoacid-generating repeat units and non-polymer-bound photoacid generator. In Table 5, the exposure latitude of Examples 26 is normalized to 1, and designated with “0”. Comparative examples which underperform relative to the example by 0-10% are designated with“”; comparative examples which underperform relative to the example by 10-20% are designated with “▪”; and comparative examples which underperform relative to the example by >20% are designated with “□”.

TABLE 5 CDU Example PAG Type Normalized Example 26 PolyPAG + Polymer-bound-PAG ⋄ Comparative Polymer-bound-PAG + free PAG ▪ Example 19 Comparative Polymer-bound-PAG + free PAG □ Example 20 Comparative Polymer-bound-PAG + free PAG ▪ Example 22

Line Width Roughness

LWR values were determined by top-down scanning electron microscopy (SEM) using a Hitachi 9380 CD-SEM, operating at an accelerating voltage of 800 volts (V), probe current of 8.0 picoamperes (pA), using 200 Kx magnification at 1.0 digital zoom, with the number of frames set to 64. LWR was measured over a 2 μm line length in steps of 40 nm, and reported as the average LWR for the measured region. The results, presented in Table 6, shows that the lowest (best) LWR values are exhibited by the inventive Examples 28 and 29. In Table 6, the LWR of Examples 28 and 29 show significant improvement over the comparative examples Improved LWR by 20-40% is designated with “▪”; and improved LWR >40% is designated with “0”. The inventive Example 28 photoresist contains photoacid generator in the form of polymer comprising 50 to 100 mole percent of photoacid-generating repeat units, and polymer comprising 50 to 100 mole percent of photoacid-generating repeat units. The inventive Example 29 photoresist composition contains photoacid generator in the form of polymer comprising 50 to 100 mole percent of photoacid-generating repeat units. The Comparative Example 30 photoresist composition contains photoacid generator in the form of a polymer comprising less than 50 mole percent of photoacid-generating repeat units. The Comparative Example 23, 24, and 25 photoresist compositions contain photoacid generator in the form of free photoacid generator.

TABLE 6 Comparative LWR Improvement @ LWR Improvement @ Example 24 nm with Example 28 24 nm with Example 29 30 □ □ 23 ▪ ▪ 24 □ □ 25 □ □

Line and Space Exposure Latitude. Exposure latitude percent (EL %) values were calculated from critical dimension (CD) data through dose and focus (FEM) with 10% CD boundaries restricted to 100 nm depth of focus (DoF) for 25 nm lines and spaces at 1:1 half pitch. The results, presented in Table 7, shows that the largest (best) exposure latitude is exhibited by the inventive Example 28. Improved performance is marked with “⇑”; similar performance is designated with“”; and inferior performance is marked with “

”.

TABLE 7 Example PAG Type EL Example 28 PolyPAG + Polymer-bound-PAG ⋄ Example 29 PolyPAG  Comparative Free PAG

Example 23 Comparative Free PAG

Example 24 Comparative Free PAG

Example 25 

1. A photoresist composition comprising: a first polymer comprising, based on 100 mole percent of total repeat units, 50 to 100 mole percent of photoacid-generating repeat units; wherein each of the photoacid-generating repeat units comprises an anion, a photoacid-generating cation, and base-solubility-enhancing functionality; wherein either the anion or the photoacid-generating cation is polymer-bound; wherein the base-solubility-enhancing functionality is selected from the group consisting of tertiary carboxylic acid esters, secondary carboxylic acid esters wherein the secondary carbon is substituted with at least one unsubstituted or substituted C₆₋₄₀ aryl, acetals, ketals, lactones, sultones, alpha-fluorinated esters, beta-fluorinated esters, alpha,beta-fluorinated esters, polyalkyleneglycols, alpha-fluorinated alcohols, and combinations thereof; and wherein the photoacid-generating cation has the structure (I)

wherein q is independently in each photoacid-generating repeat unit 0, 1, 2, 3, 4, or 5; r is independently at each occurrence in each photoacid-generating repeat unit 0, 1, 2, 3, or 4; R¹ is independently at each occurrence in each photoacid-generating repeat unit halogen, unsubstituted or substituted C₁₋₄₀ hydrocarbyl, or unsubstituted or substituted C₁₋₄₀ hydrocarbylene; m is independently in each photoacid-generating repeat unit 0 or 1; X is independently in each photoacid-generating repeat unit a single bond, —O—, —S—, —C(═O)—, —C(R²)₂—, —C(R²)(OH)—, —C(═O)O—, —C(═O)N(R²)—, —C(═O)C(═O)—, —S(═O)—, or —S(═O)₂—, wherein R² is independently at each occurrence hydrogen or C₁₋₁₂ hydrocarbyl; and Z⁻ is free or monovalent monoanion; and a second polymer that exhibits a change in solubility in an alkali developer under the action of acid.
 2. The photoresist composition of claim 1, wherein the first polymer comprises 95 to 100 mole percent of the photoacid-generating repeat units.
 3. The photoresist composition of claim 1, wherein the photoacid-generating repeat units are derived from a single monomer.
 4. The photoresist composition of claim 1, wherein the photoacid-generating repeat units are derived from at least two different monomers.
 5. The photoresist composition of claim 1, wherein the base-solubility-enhancing functionality is a tertiary carboxylic acid ester, an acetal, a ketal, a lactone, or a combination thereof.
 6. The photoresist composition of claim 1, wherein each of the photoacid-generating repeat units of the first polymer independently has the structure

wherein R³ is independently in each of the repeat units H, F, —CN, C₁₋₁₀ alkyl, or C₁₋₁₀ fluoroalkyl; n is independently in each of the repeat units 0 or 1; L¹ and L³ are each independently in each of the repeat units an unsubstituted or substituted C₁₋₂₀ hydrocarbylene, wherein the substituted C₁₋₂₀ hydrocarbylene can, optionally, comprise one or more in-chain divalent heteroatom-containing groups that is —O—, —S—, —NR⁴, —PR⁴—, —C(O)—, —OC(O)—, —C(O)O—, —OC(O)O—, —N(R⁴)C(O)—, —C(O)N(R⁴)—, —OC(O)N(R⁴)—, —N(R⁴)C(O)O—, —S(O)—, —S(O)₂—, —N(R⁴)S(O)₂—, —S(O)₂N(R⁴)—, —OS(O)₂—, or —S(O)₂O—, wherein R⁴ is H or C₁₋₁₂ hydrocarbyl; L² is independently in each of the repeat units —O—, —C(O)—, or —N(R⁵)—, wherein R⁵ is H or C₁₋₁₂ hydrocarbyl; and q, r, R¹, m, and X are defined as in claim
 1. 7. The photoresist composition of claim 1, wherein in each of the photoacid-generating repeat units one occurrence of R¹ is present, covalently links the photoacid-generating cation to the polymer, and has the structure

wherein R³ is independently in each of the repeat units H, F, —CN, C₁₋₁₀ alkyl, or C₁₋₁₀ fluoroalkyl; L⁴ is independently in each of the repeat units 1,2-phenylene, 1,3-phenylene, 1,4-phenylene, —C(O)O—, —C(O)C(O)—, or —C(O)N(R⁵)—, wherein R⁵ is H or C₁₋₁₂ hydrocarbyl; p is independently in each of the repeat units 0 or 1; and L⁵ is independently in each of the repeat units an unsubstituted or substituted C₁₋₂₀ hydrocarbylene, wherein the substituted C₁₋₂₀ hydrocarbylene can, optionally, comprise one or more in-chain divalent heteroatom-containing groups that is —O—, —S—, —NR⁴, —PR⁴—, —C(O)—, —OC(O)—, —C(O)O—, —OC(O)O—, —N(R⁴)C(O)—, —C(O)N(R⁴)—, —OC(O)N(R⁴)—, —N(R⁴)C(O)O—, —S(O)—, —S(O)₂—, —N(R⁴)S(O)₂—, —S(O)₂N(R⁴)—, —OS(O)₂—, or —S(O)₂O—, wherein R⁴ is H or C₁₋₁₂ hydrocarbyl.
 8. The photoresist composition of claim 1, wherein the first polymer comprises a homopolymer of 5-(4-methoxy-3-(4-((2-methyladamantan-2-yl)oxy)-1-(2-((2-methyladamantan-2-yl)oxy)-2-oxoethoxy)-1,4-dioxobutan-2-yl)phenyl)-dibenzothiophenium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate, a homopolymer of 5-(4-methoxy-3-(4-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-1-(2-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-2-oxoethoxy)-1,4-dioxobutan-2-yl)phenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(2-(methacryloyloxy)acetoxy)ethanesulfonate, a homopolymer of 5-(4-methoxy-3-(2-(2-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-2-oxoethoxy)-2-oxo-1-(2-oxotetrahydrofuran-3-yl)ethyl)phenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate, a copolymer of 5-(4-(2-(2-methoxyethoxy)ethoxy)-3,5-dimethylphenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate and 5-(4-methoxy-3-(4-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-1-(2-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-2-oxoethoxy)-1,4-dioxobutan-2-yl)phenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(2-(methacryloyloxy)acetoxy)ethanesulfonate, a copolymer 5-(4-(2-(2-methoxyethoxy)ethoxy)-3,5-dimethylphenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate and 5-(4-methoxy-3-(2-(2-(((1R,3S,5r,7r)-2-methyladamantan-2-yl)oxy)-2-oxoethoxy)-2-oxo-1-(2-oxotetrahydrofuran-3-yl)ethyl)phenyl)-5H-dibenzo[b,d]thiophen-5-ium 1,1-difluoro-2-(methacryloyloxy)ethanesulfonate, or a combination thereof.
 9. The photoresist composition of claim 1, wherein each of the photoacid-generating repeat units of the first polymer has the structure

wherein R³ is independently in each of the photoacid-generating repeat units hydrogen or methyl; L² is —O— in each of the photoacid-generating repeat units; L³ is independently in each of the photoacid-generating repeat units an unsubstituted or substituted C₁₋₂₀ hydrocarbylene, wherein the substituted C₁₋₂₀ hydrocarbylene can, optionally, comprise one or more in-chain divalent heteroatom-containing groups that is —O—, —OC(O)—, or —C(O)O—; and q is independently in each of the photoacid-generating repeat units 1, 2, or 3; r is zero at each occurrence in each of the photoacid-generating repeat units; at least one occurrence of R¹ in each of the photoacid-generating repeat units comprises a tertiary carboxylic acid ester, an acetal, or a ketal; m is 1 in each of the photoacid-generating repeat units; and X is a single bond in each of the photoacid-generating repeat units; and wherein the second polymer comprises 10 to 65 mole percent of acid-labile repeat units, 0 to 50 weight percent of base-labile repeat units, 0 to 40 mole percent of base-soluble repeat units, and 0 to 15 mole percent of photoacid-generating repeat units; and wherein the photoresist composition comprises, on a dry weight basis, 20 to 80 weight percent of the first polymer, 10 to 60 weight percent of the second polymer, and 0.5 to 10 weight percent of a quencher.
 10. A method of forming an electronic device, comprising: (a) applying a layer of the photoresist composition of claim 1 on a substrate; (b) pattern-wise exposing the photoresist composition layer to activating radiation; and (c) developing the exposed photoresist composition layer to provide a resist relief image. 